| Contact » |
|
| Staff » |
|
| Company Profile » |
|
|
| Services Overview » |
|
| Corrosion Control » |
|
| Failure Analysis » |
|
| Laboratory Testing » |
|
| Materials Consulting » |
|
| Field Metallography » |
|
| Fitness For Service » |
|
| Legal Consulting Services » |
|
| Risk Based Inspection » |
|
| API Storage Tank Services » |
|
| Education and Courses » |
|
| Capital Project Services » |
|
| Environmental Services » |
|
|
| Material Property Data » |
|
| Special Corrosion Topics » |
|
| Corrosion Photographs » |
|
| Corrosion Glossary » |
|
| Technical Newsletters » |
|
| Failure Case Histories » |
|
| Industry Links » |
|
| Technical Search Gateway » |
|
|
| Discussion Forums » |
|
| Technical FAQs » |
|
|
| Technical Papers » |
|
| Industry Standards » |
|
| RBI Procedure » |
|
| Printable Brochures » |
|
|
| Site Map » |
|
| Index » |
|
| Search » |
|
| Home » |
|
|
|
|
|
Chemical Compositions of Stainless Steels
| Wrought Stainless Steels |
| Alloy |
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
Others |
| 201 |
0.15 |
6.50 |
0.060 |
0.030 |
1.00 |
17.00 |
4.50 |
- |
0.25N |
| 202 |
0.15 |
9.00 |
0.060 |
0.030 |
1.00 |
18.00 |
5.00 |
- |
0.25N |
| 301 |
0.15 |
2.00 |
0.045 |
0.030 |
1.00 |
17.00 |
7.00 |
- |
- |
| 302 |
0.15 |
2.00 |
0.045 |
0.030 |
1.00 |
18.00 |
9.00 |
- |
- |
| 303 |
0.15 |
2.00 |
0.20 |
0.15 |
1.00 |
18.00 |
9.00 |
0.60 |
- |
| 303Se |
0.15 |
2.00 |
0.20 |
0.06 |
1.00 |
18.00 |
9.00 |
0.60 |
0.15Se |
| 304 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
19.00 |
9.25 |
- |
- |
| 304L |
0.03 |
2.00 |
0.045 |
0.030 |
1.00 |
19.00 |
10.0 |
- |
- |
| 309S |
0.08 |
2.00 |
0.045 |
0.030 |
0.75 |
23.00 |
13.5 |
- |
- |
| 310S |
0.08 |
2.00 |
0.045 |
0.030 |
1.50 |
25.00 |
20.5 |
- |
- |
| 316 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
17.00 |
12.0 |
2.5 |
- |
| 316L |
0.03 |
2.00 |
0.045 |
0.030 |
1.00 |
17.00 |
12.0 |
2.5 |
- |
| 317 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
19.00 |
13.0 |
3.5 |
- |
| 317L |
0.03 |
2.00 |
0.045 |
0.030 |
1.00 |
19.00 |
13.0 |
3.5 |
- |
| 321 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
18.00 |
10.5 |
- |
Ti 5 X C |
| 329 |
0.10 |
2.00 |
0.045 |
0.030 |
1.00 |
27.50 |
4.5 |
1.50 |
- |
| 330 |
0.08 |
2.00 |
0.040 |
0.030 |
1.00 |
18.50 |
35.5 |
- |
- |
| 347 |
0.08 |
2.00 |
0.045 |
0.030 |
1.00 |
18.00 |
11.0 |
- |
Cb+Ta 10 X C |
| 409 |
0.08 |
1.00 |
0.045 |
0.045 |
1.00 |
11.50 |
- |
- |
Ti 6 x C |
| 410 |
0.15 |
1.00 |
0.040 |
0.030 |
1.00 |
12.50 |
- |
- |
- |
| 416 |
0.15 |
1.25 |
0.040 |
- |
1.00 |
13.00 |
- |
0.60 |
S =0.15 min. |
| 416Se |
0.15 |
1.25 |
0.060 |
0.060 |
1.00 |
13.00 |
- |
- |
0.15 Se |
| 420 |
0.15 min. |
1.00 |
0.040 |
0.030 |
1.00 |
13.00 |
- |
- |
- |
| 430 |
0.12 |
1.00 |
0.040 |
0.030 |
1.00 |
17.00 |
- |
- |
- |
| 440C |
1.00 |
1.00 |
0.040 |
0.030 |
1.00 |
17.00 |
- |
- |
- |
| 442 |
0.20 |
1.00 |
0.040 |
0.030 |
1.00 |
20.50 |
- |
- |
- |
| 904L |
0.02 |
2.00 |
0.045 |
0.035 |
1.00 |
21.00 |
25.5 |
4.5 |
Cu 1.5 |
| 17-4 PH |
0.07 |
1.00 |
0.045 |
0.035 |
1.00 |
16.5 |
5.5 |
- |
Cu 3-5, 0.4 Al |
| 17-7 PH |
0.09 |
1.00 |
0.045 |
0.035 |
1.00 |
17.0 |
7.0 |
- |
.75-1.5 Al |
| 2205 |
0.03 |
2.00 |
0.030 |
0.020 |
1.00 |
22.0 |
5.5 |
3.0 |
0.15 N |
| Cast Stainless Steels |
| CA-6NM |
0.06 |
1.00 |
0.045 |
0.035 |
1.00 |
12.50 |
4.00 |
0.70 |
- |
| CA-15 |
0.15 |
1.00 |
- |
- |
1.50 |
12.50 |
1.00 |
- |
- |
| CA-40 |
0.40 |
1.00 |
- |
- |
1.50 |
12.50 |
1.00 |
- |
- |
| CF-3 |
0.03 |
1.50 |
0.040 |
0.040 |
2.00 |
19.00 |
10.00 |
- |
- |
| CF-3M |
0.03 |
1.50 |
0.040 |
0.040 |
1.50 |
19.00 |
10.00 |
2.5 |
- |
| CF-8 |
0.08 |
1.50 |
0.040 |
0.040 |
2.00 |
19.00 |
9.00 |
- |
- |
| CF-8M |
0.08 |
1.50 |
0.040 |
0.040 |
2.00 |
19.50 |
10.00 |
2.5 |
- |
| CH-20 |
0.20 |
1.50 |
0.040 |
0.040 |
1.50 |
20.00 |
10.00 |
- |
- |
| CK-20 |
0.20 |
2.00 |
0.040 |
0.040 |
2.00 |
25.00 |
20.00 |
- |
- |
| HF |
0.30 |
2.00 |
0.040 |
0.040 |
2.00 |
19.00 |
9.00 |
- |
- |
| HH |
0.35 |
2.00 |
0.040 |
0.040 |
2.00 |
25.00 |
12.00 |
- |
0.2 N |
| HK |
0.30 |
2.00 |
0.040 |
0.040 |
2.00 |
25.00 |
20.00 |
- |
- |
 |
|